PERMABOND UV610
Harmonization Code : 3907.30.00.40 | Epoxy Mold Compounds containing by weight more than 70 % silicon dioxide
Main features
- Fast Low-Power UV Cure
- High-Strength Glass-Metal Bonding
- Solvent-Free Cure-On-Demand Processing
Product Description
Permabond UV610 is a single-part, 100% solids methacrylate adhesive developed for UV-curing glass-to-metal assemblies. Its translucent, 600 to 1,300 mPa s viscosity supports direct bottle application or controlled automated dispensing. Depending on lamp output and substrate transmission, typical fixture time ranges from 10 seconds with a 4 mW/cm^2 battery lamp to 1 second with a 30 W/cm^2 light guide across a 365 to 400 nm cure range. The cured adhesive provides typical steel-to-glass tensile strength of 13 to 16 N/mm^2 and 95% elongation, supporting glass furniture and high-strength edge joints.
Key features
- Fast Low-Power UV Cure: Fixtures in 10 seconds with a 4 mW/cm^2 battery lamp under stated conditions.
- High-Strength Glass-to-Metal Bonding: Provides typical steel-to-glass tensile strength of 13 to 16 N/mm^2.
- 100% Solids Formulation: Uses a solvent-free, single-part formulation for cure-on-demand processing.
Applications
Applications include glass-to-metal bonding, glass furniture assembly, and high-strength glass edge joints with direct UV exposure.
Technical Specifications
No specifications available.
Additional Information
As-supplied / before-processing properties
Fixture time depends on lamp power, spectral output, distance, and substrate transmission.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Chemical composition | Methacrylate ester | As supplied | |
| Appearance | Translucent | As supplied | |
| Viscosity | 600 to 1,300 | mPa s | At 25 deg C; 20 rpm |
| Specific gravity | 1.0 | As supplied | |
| Fixture time | 10 | seconds | 4 mW/cm^2 battery lamp |
| Fixture time | 2 | seconds | 100 mW/cm^2 LED lamp |
| Fixture time | 1 | second | 30 W/cm^2 UV light guide |
| Cure wavelength | 365 to 400 | nm | Match lamp output to the photoinitiator |
After-processing / final-state properties
Strength values are typical cured results for the stated substrate and test methods.
| Property | Value | Unit | Method / condition |
|---|---|---|---|
| Steel-to-glass tensile strength | 13 to 16 | N/mm^2 | ASTM D-2095-69 |
| Tensile strength | 17 | N/mm^2 | ISO 37 |
| Refractive index | >1.490 | Cured adhesive | |
| Elongation | 95 | % | ISO 37 |
| Hardness | 65 to 75 | Shore D | ISO 868 |
| Dielectric strength | 12 | kV/mm | Typical cured value |
| Dielectric constant | 4 | 1 MHz at 25 deg C | |
| Water absorption | 3 | % | ISO 62; 2 hours in boiling water |